                      Borealis Daplen? EF040AE TPO Compound

                      Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polypropylene (PP) , TPO
                      Manufacturer Borealis
                      Trade Name Daplen?
                      Port Ningbo port,China
                      Trade Terms FOB, CFR, CIF
                      Payment Terms L/C, T/T, Western Union
                      Download PDF Borealis Daplen? EF040AE TPO Compound.pdf
                      Price EMAIL US    sales@www.akotv.net
                        Online Service   lookpolymers   27660005
                      Material Notes:
                      Daplen EF040AE is a elastomer modified polypropylene compound intended for injection molding. Daplen EF040AE is a material with excellent impact/stiffness ratio. Thanks to its low thermal expansion this material is suitable to mold parts requiring low change of dimensions over a broad temperature range. The product is optimized to give good surface aesthetics..Daplen EF040AE has been developed for automotive exterior applications, bumpers, and exterior trims.Information provided by the Manufacturer.
                      Physical Properties Metric English Comments
                      Density 0.910 g/cc
                      0.0329 lb/in3
                      ISO 1183
                      Linear Mold Shrinkage 0.0095 cm/cm
                      0.0095 in/in
                      Borealis Method
                      Melt Flow 22 g/10 min

                      @Load 2.16 kg,
                      Temperature 230 °C
                      22 g/10 min

                      @Load 4.76 lb,
                      Temperature 446 °F
                      ISO 1133
                      Mechanical Properties Metric English Comments
                      Tensile Strength, Yield 18.0 MPa
                      2610 psi
                      At 50 mm/min; ISO 527-2
                      Elongation at Break 330 %
                      330 %
                      At 50 mm/min; ISO 527-2
                      Elongation at Yield 8.5 %
                      8.5 %
                      At 50 mm/min; ISO 527-2
                      Tensile Modulus 1.04 GPa
                      151 ksi
                      At 1 mm/min; ISO 527-2
                      Flexural Strength 21.0 MPa
                      3050 psi
                      ISO 178
                      Flexural Modulus 1.05 GPa
                      152 ksi
                      At 2 mm/min; ISO 178
                      Charpy Impact Unnotched NB
                      NB
                      ISO 179/1eU
                      NB

                      @Temperature -20.0 °C
                      NB

                      @Temperature -4.00 °F
                      ISO 179/1eU
                      Charpy Impact, Notched 4.00 J/cm2
                      19.0 ft-lb/in2
                      ISO 179/1eA
                      0.400 J/cm2

                      @Temperature -30.0 °C
                      1.90 ft-lb/in2

                      @Temperature -22.0 °F
                      ISO 179/1eA
                      0.550 J/cm2

                      @Temperature -20.0 °C
                      2.62 ft-lb/in2

                      @Temperature -4.00 °F
                      ISO 179/1eA
                      Thermal Properties Metric English Comments
                      Deflection Temperature at 0.46 MPa (66 psi) 88.0 °C
                      190 °F
                      ISO 75-2
                      Vicat Softening Point 138 °C
                      280 °F
                      A (10N); ISO 306
                      Shrinkage 0.150 %

                      @Temperature 90.0 °C,
                      Time 7200 sec
                      0.150 %

                      @Temperature 194 °F,
                      Time 2.00 hour
                      Post Shrinkage; Borealis Method
                      Processing Properties Metric English Comments
                      Melt Temperature 220 - 260 °C
                      428 - 500 °F
                      Polymer Mass Temp
                      Mold Temperature 30.0 - 50.0 °C
                      86.0 - 122 °F