                      Songhan Plastic Technology Co.,Ltd.
                       POLYMER SEARCH

                      LATI LATILUB 95-25GR CE/10 Polysulfone Base (PSU), 25% Graphite, 10% Special Mineral Filled Self Lubricating Plastic

                      Category Polymer , Thermoplastic , Polyarylsulfone (PAS) , Polyarylsulfone; Molded/Extruded , Polysulfone (PSU)
                      Manufacturer
                      Trade Name
                      Port Shanghai port,China
                      Trade Terms FOB, CFR, CIF
                      Payment Terms L/C, T/T, Western Union
                      Download PDF LATI LATILUB 95-25GR CE/10 Polysulfone Base (PSU), 25% Graphite, 10% Special Mineral Filled Self Lubricating Plastic.pdf
                      Price EMAIL US    sales@www.akotv.net
                        Online Service   lookpolymers   27660005
                      Material Notes:
                      Description: Latilub self-lubricating plastic materials are more and more often designed to replace metals in applications such as gears, bushings, cams, slides, etc), for which, besides their intrinsic properties (moldability, low cost, lightness, high mechanical properties), low friction coefficient and low wear are required.Specific Notes for this Material: polysulfone base (PSU); 25% graphite; good wear resistance even at high temperature; 10% special mineral fillers; excellent dimensional stability; resistant to hot water.Disclaimer from LATI: This document contains information based on average values as obtained from the results of laboratory tests and observations made on LATI materials. Tested materials were injection molded, used in their natural color, and conditioned in compliance with Standard ASTM D 618, procedure A. These values refer to LATI's best technical and scientific knowledge at the moment of testing and cannot be used as a basis for the development of applications. For a better assessment of the materials, you are kindly requested to contact LATI's technical or commercial offices, which are at your disposal and will supply detailed information on the most suitable characteristics for their intended use. With reference to DPR n.224 dated May 24, 1988, issued in accordance with EC Guide-lines 85/374, LATI Industria Termoplastici S.p.A. declines all responsibility arising from an improper use of the products described in this document.All data provided by LATI.
                      Physical Properties Metric English Comments
                      Density 1.48 g/cc
                      0.0535 lb/in3
                      ISO 1183
                      Water Absorption 0.20 %
                      0.20 %
                      at 23°C; ISO 62
                      Linear Mold Shrinkage 0.0025 cm/cm
                      0.0025 in/in
                      LATI
                      Linear Mold Shrinkage, Transverse 0.0025 cm/cm
                      0.0025 in/in
                      LATI
                      Mechanical Properties Metric English Comments
                      Tensile Strength, Ultimate 60.0 MPa
                      8700 psi
                      ISO 527
                      Flexural Modulus 7.70 GPa
                      1120 ksi
                      ASTM D790
                      Izod Impact, Notched 0.300 J/cm

                      @Temperature 23.0 °C
                      0.562 ft-lb/in

                      @Temperature 73.4 °F
                      ASTM D256
                      Charpy Impact Unnotched 0.800 J/cm2

                      @Temperature 23.0 °C
                      3.81 ft-lb/in2

                      @Temperature 73.4 °F
                      DIN 53453
                      Thermal Properties Metric English Comments
                      Deflection Temperature at 0.46 MPa (66 psi) 177 °C
                      351 °F
                      ASTM D648
                      Deflection Temperature at 1.8 MPa (264 psi) 172 °C
                      342 °F
                      ASTM D648
                      Vicat Softening Point 180 °C
                      356 °F
                      50°C/h 50N; ISO 306
                      Flammability, UL94 HB

                      @Thickness 1.50 mm
                      HB

                      @Thickness 0.0591 in
                      Processing Properties Metric English Comments
                      Melt Temperature 300 - 330 °C
                      572 - 626 °F
                      Mold Temperature 100 - 120 °C
                      212 - 248 °F
                      Drying Temperature 120 - 130 °C
                      248 - 266 °F
                      Temperature can be reduced when using vacuum ovens.
                      Dry Time >= 3 hour
                      >= 3 hour
                      Drying time can be reduced when using vacuum ovens.
                      Descriptive Properties Value Comments
                      Heat Resistance - Ball Test (125°C) Y
                      IEC 335
                      Heat Resistance - Ball Test (165°C) Y
                      IEC 335
                      Injection Speed high
                      Needle Burner Test Y
                      1.47 mm
                      Y
                      3.05 mm